| 在乙醇介质中、碱催化下、以间苯二酚和甲醛为原料合成了部分水解聚丙烯酰胺凝胶化所用交联剂,考察了反应介质、反应物摩尔配比、反应温度以及地层温度等因素的影响。结果 表明:①间苯二酚和甲醛在介电常数小于水的有机溶剂中进行反应可以使交联有效期显著延长；②间苯二酚与甲醛以摩尔比为1.0 ∶2.0反应得到的交联剂与部分水解聚丙烯酰胺所成凝胶在黏度和强度方面优于其他反应物配比；③间苯二酚与甲醛在40 ℃下反应有利于间苯二酚发生羟甲基化并生成甲阶树脂,可以有更多的交联位点与部分水解聚丙烯酰胺发生交联反应；④合成的间苯二酚-甲醛树脂与部分水解聚丙烯酰胺所形成的凝胶适用于50～90 ℃的地层温度。 |
| 关键词: 凝胶 聚丙烯酰胺 间苯二酚 甲醛 交联剂 |
| DOI：10.3969/j.issn.1007-3426.2013.04.013 |
| 分类号:TE357.1+2 |
| 基金项目:国家科技重大专项“低渗透油藏中高含水期稳产配套技术”(2011ZX05013-005)。 |
|
| Synthesis of resorcinol-formaldehyde resin and its gellation performance with HPAM |
|
Bi Weiyu1,2, Chen Na3, Wang Xinghong1,2
|
|
(1. Research Institute of Oil and Gas Technology, PetroChina Changqing Oilfield Company, Xi'an 710021,Shaanxi,China;2. National Engineering Laboratory for Exploration and Development of Oil and Gas Fields with Low Permeability, Xi'an 710021, Shaanxi, China;3. No.1 Oil Production Plant, PetroChina Changqing Oilfield Company, Yan'an 716000, Shaanxi,China)
|
| Abstract: |
| The crosslinker for gellation of partly hydrolyzed polyacrylamide was synthesized by the reactants of resorcinal and formaldehyde in ethanol, with alkali as catalysts. The effects of solvent, molar ratio, reaction temperature and formation temperature on gellation were studied. The results showed that:①the time span for effective crosslinking of HPAM was prolonged profoundly when the organic solvents with dielectric constant smaller than that of water were adopted as reaction media;②the HPAM gel with optimum viscosity and strength was obtained when the crosslinker was synthesized from resorcinal and formaldehyde in the molar ratio of 1.0 ∶ 2.0; ③the reaction temperature of 40 ℃ was conducive to the hydroxymethylation of resorcinal and formation of A-stage resin, by which more active sites were available for crosslinking with HPAM; ④the gel formed from HPAM and resorcinal-formaldehyde resin can be applied for the formation with temperature in the range of 50 ℃ to 90 ℃. |
| Key words: gel polyacrylamide resorcinol formaldehyde crosslinker |