引用本文: | 袁曦,肖杰,张碧波,王星,朱庆,蔡德强,等. 酸性气井井筒腐蚀控制技术研究[J]. 石油与天然气化工, 2017, 46(1): 76-78, 82. |
| |
|
摘要: |
采用高温高压腐蚀挂片、气田水化学分析、多臂井径仪测井等方法,在含H2S /CO2酸性气井中,研究了缓蚀剂对井下油管的保护效果。试验结果表明,评选的缓蚀剂防腐效果良好,井下加入缓蚀剂4年后,全油管平均腐蚀速率为0.04 mm/a,腐蚀速率远低于腐蚀控制指标0.1 mm/a;油管腐蚀主要集中在井筒上部和底部。 |
关键词: 井筒 硫化氢 二氧化碳 腐蚀 缓蚀剂 |
DOI:10.3969/j.issn.1007-3426.2017.01.015 |
分类号: |
基金项目: |
|
Study on wellbore corrosion control technology in sour gas wells |
Yuan Xi1, Xiao Jie1, Zhang Bibo2, Wang Xing2, Zhu Qing2, Cai Deqiang2, Wang Meng2
|
1. Research Institute of Natural Gas Technology, PetroChina Southwest Oil and Gasfield Company, Chengdu, Sichuan, China;2. Southern Sichuan Gas District, PetroChina Southwest Oil and Gasfield Company, Luzhou, Sichuan, China
|
Abstract: |
Using methods of corrosion coupon in high temperature and high pressure, chemistry analysis of gas water and multi-arm caliper logging tool, the application effects of corrosion inhibitor were studied on H2S/CO2 gas well. Test resuilts showed that the selected corrosion inhibitor has good effect of anti-corrosion, after addition of corrosion inhibitor for 4 years, the corrosion rate of full tubing was 0.04 mm/a, lower than 0.1 mm/a corrosion control standard; the corrosion areas were mainly concentrated at the top and bottom of the tubing. |
Key words: wellbore H2S CO2 corrosion corrosion inhibitor |